| 钨铜药型罩制备及其侵彻性能研究 |
| On the Preparation and Penetration Performance of Tungsten-Copper Shaped Charge Liner |
| Received:December 10, 2011 Revised:May 09, 2012 |
| DOI： |
| 中文关键词: 钨铜药型罩 聚能装药 聚能粒子流 |
| 英文关键词:W-Cu shaped charge liner shaped charge shaped charge granular jet |
| 基金项目:国家自然科学基金(11072222)(51174183)和(51134012)资助 |
| Author Name | Affiliation | | LIU Ying-bin* | 1.Department of Modern Mechanics, University of Science and Technology of China, Hefei 230027, China
2.School of Chemistry and Environment Engineering North University of China, Taiyuan 030051, China | | SHEN Zhao-wu | Department of Modern Mechanics, University of Science and Technology of China, Hefei 230027, China | | LIU Tian-sheng | School of Chemistry and Environment Engineering North University of China, Taiyuan 030051, China | | HU Xiao-yan | Department of Modern Mechanics, University of Science and Technology of China, Hefei 230027, China | | SUN Su-jie | Science and Technology on Materials in Impact Environment Laboratory Yantai Sub-institute of China Ordnance Industries Group Corporation, Yantai 264003, China |
|
| Hits: 111103 |
| Download times: 1323 |
| 中文摘要: |
| 为了提高钨铜药型罩的侵彻性能和稳定性,在传统钨铜制备方法的基础上,采用机械合金化方法进行混粉,利用旋模压制方法进行压制药型罩毛坯,再在甲醇裂解气体的保护下进行烧结,最终制备出钨铜药型罩。利用排水法测试了烧结前后钨铜药型罩的密度。并将制备出的钨铜药型罩与紫铜板药型罩进行侵彻性能的实验比较。实验结果表明:钨铜药型罩烧结后的密度比烧结前的密度要低一些,但其对603均质装甲钢的侵彻性能要优于紫铜板药型罩的侵彻性能,与紫铜板药型罩相比,其穿深可以提高45%。 |
| 英文摘要: |
| In order to improve the penetration performance and stability of tungsten-copper shaped charge liner, a new W-Cu shaped charge liner was prepared. Based on the traditional tungsten-copper preparation method, a series of new technology was adopted including using mechanical alloying method to mix powder, using spin-mode suppression method to press the blank of shaped charge liner then sintered under the protection of methanol cracking gas. Density of W-Cu shaped charge liner before and after sintering was tested by drainage method. The penetration performance was compared experimentally between the W-Cu shaped charge liner and the copper plate shaped charge liner. Results show that the density of W-Cu shaped charge liner after sintering is lower than the density before sintering; for 603 homogeneous armor steel plate, the penetration performance of W-Cu shaped charge liner is superior to copper shaped charge liner, and the penetration depth increases up to 45% compared with copper plate shaped charge liner. |
| View Full Text Download reader |